Products Description
Recently, the electrolytic production of hypochlorous acid and sodium hypochlorite generally adopts a diaphragmless electrolytic cell. Such a structure of hypochlorous acid and sodium hypochlorite generating device is easy to release a lot of heat when electrolyzing dilute brine, causing the electrolyte temperature in the electrolytic cell to rise quickly, resulting in a decrease in the concentration of effective chlorine in the electrolyte: Accelerating the flow of dilute brine and shortening the reaction time can also solve the temperature rise problem, but it will cause the electrolysis of sodium chloride to be untimely, the concentration of hypochlorous acid and sodium hypochlorite is low, and the salinity is high.
The existing technology generally adopts the cooling system around the diaphragmless electrolytic cell to alleviate the problem of electrolyte temperature rise, but it has not been able to completely solve the problem of suitable electrolyte temperature. At present, the conversion rate of hypochlorous acid and sodium hypochlorite is often only 40-50%, and the power consumption is high. The use of ion membrane electrolysis can effectively improve the conversion rate of hypochlorous acid and sodium hypochlorite, but the ion membrane has the disadvantages of short service life, frequent alternating use, easy to cause failure, high production cost, low output of hypochlorous acid and sodium hypochlorite, slow reaction speed, etc. Therefore, improving the sodium hypochlorite conversion rate of diaphragm-free hypochlorous acid and sodium hypochlorite generating devices has become a technical problem that technicians in the relevant technical field urgently need to solve.
| Some product parameters | |
|---|---|
| Effective chlorine output | 50-3000g/h single tank, can be connected in series and parallel |
| Effective chlorine concentration | ≤8500ppm |
| Plate material | Ti-Ru system mixed coating |
| Design life | 3-5 years and above |
| Current efficiency | ≥85% |
| Support OEM/ODM | |
Solution: dilute hydrochloric acid or dilute hydrochloric acid + sodium chloride
Cell body material: PMMA/ABS/PTFE
Plate material: titanium-based ruthenium-plated electrode plate
Effective chlorine concentration: 50-200ppm
When using diaphragmless electrolyzer, the sodium chloride solution of a certain concentration can be prepared with dilute hydrochloric acid and input into the electrolyzer through a constant current pump. The solution components after the electrolysis reaction in the tank are mainly dissolved Cl2, H2, Na+, H+, Cl-, ClO-, HClO. After the liquid flows out through the pipeline, it reacts with a certain proportion of tap water in another reactor to convert into hypochlorous acid solution. In this process, the operating conditions such as the ratio concentration, pH value and electric density of the electrolyte will affect the concentration of hypochlorous acid. Therefore, the electrolysis operating parameters are optimized according to needs to prepare the ideal hypochlorous acid concentration.
Specification: 240*50mm x 1mm;
Anode substrate: Titanium in Gr1;
Anode Coating: Platinum;
Coating Thickness: 5 Micron;
Shape: Mesh;
Size: As per the drawing;
Application: Electroplating;
Export Country: South Korea.
Products show
Company introduction
FOCUSED ON HIGH OUALITY TITANIUM MATERIAL
The Baoji JM-TITANIUM Metal company developed and produced the ruthenium-iridium-coated titanium electrodes and the platinum-coated titanium electrodes. These electrodes, which use imported ionic membranes, have a stable electrolysis effect and are widely used in home water electrolysis machines, disinfection water machines, and large water With its low energy efficiency, consistent electrolysis, long lifespan, low cost, and successful passing of the EU's EC-1935-2004 test, the factory has gained popularity and been put to use.
Product Process
1. Purchase the GR1 titanium substrate to ensure that the surface of the plate is smooth and flat, without deep scratches and defects.
2. Machining the purchased titanium substrate and processing it to the size required by the customer.
3. Annealing and leveling the titanium substrate at a temperature of >500 °C. (To eliminate stress and ensure flatness.)
4. When the annealing leveling treatment, a dense titanium oxide layer is formed on the surface of the titanium substrate, and it is polished by mechanical or artificial means, and the surface thereof is made of titanium metallic luster.
5. The titanium substrate is subjected to pickling etching with 10% strength oxalic acid, and is subjected to a micro-boiling state for several hours to etch the surface oxide layer into a titanium hydride surface.
6. Qualitative and quantitative configuration of the precious metal solution according to the anode environment applied by the customer.
7. Detecting that the pickled titanium substrate is qualified, that is, the surface layer is gray uniform matte structure, and then manually coating and arranging, sintering at a set temperature, sintering naturally, cooling, and cooling to normal temperature for a second coating Resume, and so on, until the configuration solution is finished after 17~20 times.
8. After the sintering of the above processed parts is completed, the life test will be carried out with the test piece of the furnace, and the qualified package will be shipped.
Working principle
This electrolyzer is diaphragmless electrolyzer. It prepares sodium hypochlorite solution online by electrolyzing low-concentration sodium chloride solution or seawater. Or it can electrolyze saline wastewater to degrade organic matter, such as COD, ammonia nitrogen, total nitrogen, decolorization, etc. The above specifications are conventional design specifications, and can also be redesigned and customized according to actual needs.
Shipping and Packing
Transportation method
Express (DHL, Fedex, UPS, national special line) air transportation, sea transportation, land transportation, multiple ways to meet your needs
Port:
Tianjin, Shanghai, Qingdao or any other Chinese main port.
Lead Time:
2-15 days after payment confirmed.
Packaging Details:
1. Inside: Kraft papers, plastic bags, polyethylene foamed sheet;
2. Outside: packing: wooden box;
3. Or according to customer requirement.
Contact
Contact us for more information. Thank you
Nicole
Company: Baoji Jimiyun Dynamic Co., Ltd
Country:China
Add:Baoti road,Jintai,Baoji city,Shaanxi,China
Cel:+86 18391896637
Gmail:Nicole@jmyunti.com
Website:www.jm-titanium.com
Hot Tags: large flow tubular electrolyzer-diaphragmless electrolyzer, China, suppliers, manufacturers, factory, customized, wholesale, buy, price, cheap, sale, quotation, in stock, free sample, crypto steel plates, titanium alloy strip, titanium square rod, titanium headset bolt, Titanium Hexagon Flange Screw, titanium grade 7 sheet