What are the manufacturing processes of titanium anode?
1. Welding
Ruthenium Anode Company will introduce to you that some products need to be welded after blanking and drilling. Titanium materials are mainly welded by argon arc welding, and only the same materials can be welded together. The plate and tube welding method is fixed by spot welding first, and then fully welded, but only spot welding can be used for the mesh.
2. Sandblasting
A treatment process in which a sandblasting machine is used to spray onto the surface of a titanium substrate with the help of compressed air power. Sand is sprayed onto the substrate for impact grinding to remove impurities, variegated colors and oxide layers on the surface. At the same time, the sand blasting machine roughens the surface of the titanium substrate, increases the effective contact area of the titanium surface, and enhances the adhesion between the coating and the titanium surface.
The main point of sandblasting is that the pockmarks and pockmarks should be evenly sprayed, and spraying should not be missed.
3. Annealing
Annealing is a metal heat treatment process in which the metal is slowly heated to a certain temperature, kept for a sufficient time, and then cooled at an appropriate speed.
When blanking, some materials are bent or deformed. We can use some methods and tools to make simple corrections so that they will not affect the next work too much. However, after the local high temperature of welding and the air pressure of sandblasting, the deformation of the titanium substrate will be obvious.
Put the board (net) on a very thick steel plate, and it is required to be placed flat and aligned with the corners. Ruthenium Anode Company reminds you to put another same steel plate on the board (mesh) with screws on the diagonal. Make the next two steel plates fully squeeze the middle plate (network). Then send it to a furnace with a temperature of about 500 to heat and correct the shape. After a certain period of time, keep it warm for 2 hours.
4. Brushing
Apply the prepared precious metal liquid evenly on the substrate with a brush, and then dry it in a drying oven, so that the liquid can quickly combine with the substrate and prevent the traces left when the liquid flows down the substrate. In the first 5 brushings, the liquid can be applied more and can fill the surface of the substrate. It is necessary to brush less liquid on the back, so that the liquid can be applied more evenly, and at the same time, it can also cover the area where the brush was painted in front, so that the coating is beautiful. It is required to wear a mask when brushing, the environment, ventilation, dust-free, especially not to see the water. To ensure the purity of the liquid and the beauty of the board surface.
5. Baking
The plates are dried, put into a furnace that has reached a certain temperature and kept warm for a certain period of time, and pulled out to cool and oxidize naturally. Then enter the next program.
Repeat the procedure: brushing, drying, heat preservation, cooling. Brushing procedure about 14~20 times
6. Cutting
After determining the shape, quantity or quality of materials required to make a certain equipment or product, the operation process of removing materials of a certain shape, quantity or quality from the whole or a whole batch of materials.
After selecting the materials, make a certain shape and quantity according to the drawings and customer requirements. Scribe, dot, mark and punch holes. Whether it needs to be polished, it must be operated strictly according to the requirements of the drawing. Reasonably plan the processing technology to reduce loss.
The cutting must be precise.
7. Dosing
According to the actual needs of customers to configure precious metal solutions. Usually the liquid preparation is prepared the day before the brush layer is planned, because the prepared liquid can only be used after a period of drying. While drying, it needs to be stirred constantly to prevent the liquid from settling.
8. Pickling
Ruthenium Anode Company will explain to you that the pickling solution of the pickling process is generally a mixture of various acids, mainly including sulfuric acid, nitric acid and hydrofluoric acid, etc. These mixed acids are highly corrosive and have strong
The oxidation resistance and high temperature of corrosive medium put forward high requirements on the corrosion resistance of anti-corrosion materials. Pour oxalic acid into boiling water according to a certain ratio, put the base material into a cooking pot for boiling and soaking. Oxalic acid can not only effectively remove the blue scale on the substrate during annealing, but also make the surface of the substrate rougher and remove surface impurities through corrosion.
Always pay attention to the changes of the titanium substrate during pickling to prevent the formation of titanium oxalate on the surface of the substrate.