Titanium alloy welding wire
Main features: The density of titanium alloy is generally around 4.51g/cm3, which is only 60% of that of steel. The strength of pure titanium is close to that of ordinary steel, and some high-strength titanium alloys exceed the strength of many alloy structural steels. The heat resistance, strength, plasticity, toughness, formability, weldability, corrosion resistance and biocompatibility of Ti-6Al-4V titanium alloy are all good. The amount of this alloy has accounted for 75%-85% of all titanium alloys.
Product Specifications
Diameter: 1.0mm-6.0mm
The surface of the welding wire is clean, no oxidation color, no cracks, peeling, thorns, marks and inclusions, etc.
material
ERTi-5 (GR5 Ti-6Al-4V )
Chemical composition standard:
| Fe | O | C | N | H | Al | V | Ti | |
| ERTi-5 GR5 | 0.22 | 0.12-0.2 | 0.05 | 0.03 | 0.015 | 5.5-6.75 | 3.5-4.5 | other |
Titanium alloy welding wire is an excellent structural material. It is widely used in aviation, aerospace, rocket, satellite, shipbuilding, chemical, metallurgy, heavy industry and other industrial sectors. It has excellent corrosion resistance, high strength, small size. high density and good heat resistance and processing properties.
Titanium alloy welding wire is widely used in occasions requiring ductility, formability and weldability, such as titanium alloy pipe welding.
Precautions:
1. Avoid atmospheric pollution during welding.
2. Before welding, chemical methods should be used to remove impurities such as oil, water and oxides on the workpiece and welding wire.
3. The end of the filler wire should be protected during welding to avoid discoloration of the end of the welding wire.
Operation essentials
1. During manual argon arc welding, the angle between the welding wire and the weldment should be kept as small as possible (10~15°). The welding wire is smoothly and evenly fed into the molten pool along the front of the molten pool, and the end of the welding wire shall not be moved out of the argon protection zone.
2. During welding, the welding torch basically does not swing laterally. When swinging is required, the frequency should be low and the swinging amplitude should not be too large to prevent the protection of argon gas from being affected.
3. When the arc is broken and the welding seam is finished, the argon gas protection should be continued until the welding seam and the metal in the heat-affected zone cool down to below 350 ℃ before removing the welding torch.
Contact us for more information. Thank you
Nicole
Company: Baoji Dynamic Trading Co., Ltd
Cuntry:China
Add:Baoti road,Jintai,Baoji city,Shaanxi,China
Cel:+86 13369210920
Gmail:nicole@jmyunti.com
Website:www.jm-titanium.com
Hot Tags: titanium alloy welding wire, China, suppliers, manufacturers, factory, customized, wholesale, buy, price, cheap, sale, quotation, in stock, free sample, titanium periodic symbol, DIN439 titanium nut, titanium alloy pipe coil, titanium bolt DIN84, titanium location on periodic table, Titanium Tent Nail